Fiberfil® PP-68/TC/20
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Fiberfil® Engineered Plastics Inc. |
| Trademark: | Fiberfil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RwgFuM_Fiberfil-PP-68-TC-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fiberfil®PP-68/TC/20 is a polypropylene copolymer (PP Copoly) material, which contains 20% talc filler. This product is available in North America,. Fiberfil®The main features of PP-68/TC/20 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 1.0 | % | ASTM D955 |
| 6.35 mm | 1.2 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 80 - 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2480 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 27.6 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 30 | % | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 2340 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 40.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 82.2 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 76.7 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 204 - 227 | °C | |
| Front Temperature | 182 - 199 | °C | |
| Nozzle Temperature | 182 - 193 | °C | |
| Processing (Melt) Temp | 199 - 232 | °C | |
| Mold Temperature | 32.2 - 71.1 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.00 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw speed: Medium to Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Primefin V500MI20 | Lucent Polymers, Inc. | PP Homopolymer | Primefin |
| Shanghai Potomer SG3 | Shanghai Potomer International Trade Co., Ltd. | PVC, Flexible | Shanghai Potomer |
| NEOPLAST 173 C | Zylog Plastalloys | TPV | NEOPLAST |
| Chemlon® 240GH | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| POLYCOMPO PP B221WA | POLYCOMPO Co.,Ltd. | PP, Unspecified | POLYCOMPO PP |