Hostacom 65F4-2

Category:	PP Homopolymer , Polypropylene Homopolymer
Manufacturer:	LyondellBasell Industries
Trademark:	Hostacom
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	RvGle5_Hostacom-65F4-2.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
Hostacom 65F4-2 conventional melt flow, 1,900 MPa flexural modulus, 20% talc-filled polypropylene homopolymer is designed for balanced stiffness, impact resistance, dimensional stability, colorability and heat aging performance.

General Information
Filler / Reinforcement	Talc, 20% Filler by Weight
Features	Good Colorability Good Dimensional Stability Good Heat Aging Resistance Good Impact Resistance Good Stiffness High Heat Resistance Homopolymer
Uses	Appliances Automotive Applications Electrical Parts Household Goods
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.05	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	4.0	g/10 min	ASTM D1238
Molding Shrinkage - Flow (23°C, 48 hr, 3.20 mm)	1.2	%	ASTM D955

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	84		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638
Yield	31.0	MPa
Break	29.0	MPa
Tensile Elongation			ASTM D638
Yield	4.0	%
Break	70	%
Flexural Modulus - Tangent ¹	1900	MPa	ASTM D790A

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	37	J/m	ASTM D256A

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	109	°C	ASTM D648

Note Message
1 .	1.3 mm/min

Resin Grade	Manufacturer	Category	Trademark
RTP 107 CC HB	RTP Company	PP, Unspecified	RTP
Cellophane™ 315PC	Innovia Films Ltd.	Cellulose, Regenerated	Cellophane™
Kumho KBR 710H	Korea Kumho Petrochemical Co., Ltd.	PBR, Low Cis	Kumho KBR
Pexidan® R/T	Saco Polymers	XLPE	Pexidan®
Sylvin 9812-65 Blue 8405	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin