AMPLIFY™ TY 1351
| Category: | MAH-g , Functional Polymer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AMPLIFY™ TY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QhB1gv_AMPLIFY-TY-1351.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AMPLIFY™ TY 1351 Functional Polymer is a maleic anhydride grafted (MAH) polymer. In tie layers for flexible packaging, AMPLIFY TY 1351 Functional Polymer promotes adhesion of Polyethylene to barrier polymers such as polyamide and other polar substrates. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.1 | g/10 min | ASTM D1238, ISO 1133 |
| MAH Graft Level 1 | Low | Internal method |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Puncture Resistance (51 µm) | 11.6 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 51 µm | 209 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 229 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 10.5 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 11.3 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 36.1 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 29.2 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 690 | % | ASTM D882 |
| TD : Fracture, 51 µm | 690 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 260 | g | ASTM D1709 |
| Elmendorf Tear Strength 2 | ASTM D1922 | ||
| MD : 51 µm | 750 | g | ASTM D1922 |
| TD : 51 µm | 1100 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 98.9 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 123 | °C | Internal method |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 70 | ASTM D2457 |
| Extrusion instructions |
|---|
| Recommended Melt Temperature - 400-446°FFabrication Conditions for Blown Film Screw Size: 2.5 in. (63.5 mm); 24:1 L/D Screw Type: Barrier screw Die Gap: 70 mil (1.8 mm) Melt Temperature: 430°F (221°C) Output: 6 lb/hr/in of die circumference Die diameter: 6 in Blow-Up Ratio: 2.5:1 Screw Speed: 70 rpm |
| Note Message | |
|---|---|
| 1 . | Low: <0.25 wt%, Medium 0.25-0.5, High >0.5 wt% |
| 2 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G0 202 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Synthos PS GP 545 | Synthos S.A. | PS (GPPS) | Synthos PS |
| THERMOLAST® K TC6SCE (Series: SCR) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Chemlon® 66GF6 | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Fainplast PVC KLT 01590 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |