Radilon® S BMX200K 333 NER
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Rqqhm0_Radilon-S-BMX200K-333-NER.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA6 high viscosity blow moulding grade. Toughened, heat stabilized. Black colour. Suitable for blow-moulding of tubes and containers; typically used for automotive air ducts. ISO 1043 : PA6-HIT |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.07 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/5.0 kg) | 3.0 | -- | g/10 min | ISO 1133 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1700 | -- | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 45.0 | -- | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 15 | -- | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | > 100 | -- | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 1500 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 60.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 25 | -- | kJ/m² | |
| 23°C | 90 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 55.0 | -- | °C | ISO 75-2/Af |
| Melting Temperature 3 | 220 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | < 30 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C | |
| Injection Rate | Moderate |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Melt Temperature | 250 to 280 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTV-2 XP-643 | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| Axiall PVC 10805 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Celstran® PP-GF40-0403 P10/10 | Celanese Corporation | PP, Unspecified | Celstran® |
| Geon™ Vinyl Flexible C8001 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| SCHULABLEND® M/MX 5301 U | A. Schulman Europe | PC+PBT | SCHULABLEND® |