KOPA® KN170SA
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | KOPA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EMgTDK_KOPAKN170SA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6 Compound resin, Extrusion grade |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.3 - 1.5 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 1.8 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 63.7 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 400 | % | ASTM D638 |
| Flexural Modulus | 1130 | MPa | ASTM D790 |
| Flexural Strength | 53.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 74 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 180 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 65.0 | °C | ASTM D648 |
| Melting Temperature | 220 | °C | |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.40 | ASTM D150 | |
| Arc Resistance | 120 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9462-80 Black | Sylvin Technologies Incorporated | PVC Alloy | Sylvin |
| Wellamid® GF33-66 XE-NBK1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Utomer UT81P95A | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyether | Utomer |
| Halene H E5201 | Haldia Petrochemicals Ltd. | HDPE | Halene H |
| LNP™ VERTON™ MV006BS compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ VERTON™ |