Category:	Fluorelastomer , Fluoroelastomer
Manufacturer:	3M Advanced Materials Division
Trademark:	3M™ Dyneon™ Fluoroelastomer
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	RqpA1v_3MDyneonFluoroelastomerFC1610N.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
3M™ Dyneon™ Fluoroelastomer FC 1610N is a dipolymer made from hexafluoropropylene and vinylidene fluoride. It is a raw gum without curatives. Special Features Composition: dipolymer of vinylidene fluoride and hexafluoropropylene Process targets: injection moulding, extrusion, calendering and coatings Low viscosity gum stock without incorporated curatives Amine and bisphenol curable Typical Applications 3M™ Dyneon™ Fluoroelstomer FC 1610N is suitable for all sorts of finished products: O-rings, moulded parts, including metal bonding products, extrudates and calendered sheets, depending on the curative package and compound recipe used.

Message

3M™ Dyneon™ Fluoroelastomer FC 1610N is a dipolymer made from hexafluoropropylene and vinylidene fluoride. It is a raw gum without curatives.

Special Features

Composition: dipolymer of vinylidene fluoride and hexafluoropropylene

Process targets: injection moulding, extrusion, calendering and coatings

Low viscosity gum stock without incorporated curatives

Amine and bisphenol curable

Typical Applications
3M™ Dyneon™ Fluoroelstomer FC 1610N is suitable for all sorts of finished products: O-rings, moulded parts, including metal bonding products, extrudates and calendered sheets, depending on the curative package and compound recipe used.

General Information
Features	Low viscosity
Uses	O-rings Metal bonding Sheet Coating application
Forms	Particle
Processing Method	Extrusion Coating Calendering Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.80	g/cm³	Internal method
Mooney Viscosity (ML 1+10, 121°C)	17	MU	Internal method
Fluorine Content	66	%	Internal method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	73		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹(100% Strain)	6.70	MPa	ASTM D412A
Tensile Strength ²	13.7	MPa	ASTM D412A
Tensile Elongation ³(Break)	170	%	ASTM D412A
Compression Set (200°C, 70 hr)	15	%	ASTM D1414

Note Message
1 .	D mould
2 .	Die D
3 .	D mould

Resin Grade	Manufacturer	Category	Trademark
Prime PE HMWPE 1000 Swirl	Primex Plastics Corporation	HMWPE	Prime PE
Altuglas® V 045	Altuglas International of Arkema Inc.	Acrylic (PMMA)	Altuglas®
Hyundai EP PA66 LD340	HYUNDAI EP Co., Ltd.	Nylon 66	Hyundai EP PA66
Kazan HDPE 293-4-7O1K	Kazanorgsintez Joint Stock Company	HDPE	Kazan HDPE
Geon™ Vinyl Flexible HC38580	PolyOne Corporation	PVC, Flexible	Geon™ Vinyl Flexible