3M™ Dyneon™ PTFE Compound TF 4216
| Category: | PTFE , Polytetrafluoroethylene |
| Manufacturer: | 3M Advanced Materials Division |
| Trademark: | 3M™ Dyneon™ PTFE Compound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gt1eFd_3M-Dyneon-PTFE-Compound-TF-4216.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Features
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.09 | g/cm³ | ASTM D4745-06 |
| Apparent Density | 0.69 | g/cm³ | ASTM D4894-07 |
| Molding Shrinkage - Flow | 1.9 | % | ASTM D4894-07 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness 1(Shore D) | 62 | DIN 53505 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Break) | 14.5 | MPa | ASTM D4745-06 |
| Tensile Elongation 3(Break) | 70 | % | ASTM D4745-06 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | 90.0 | MPa | |
| Compression Molding Temperature | 23 to 26 | °C | |
| Sintering Temperature | < 365 | °C |
| Note Message | |
|---|---|
| 1 . | Measured on sintered moldings |
| 2 . | Measured on sintered moldings |
| 3 . | Measured on sintered moldings |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUSTAMID 6G PD 120 | Röchling Sustaplast SE & Co. KG | Nylon 6 | SUSTAMID |
| Multiuse Leostomer® LE-3150N | Riken Technos Corp. | TPU, Unspecified | Multiuse Leostomer® |
| Eltex® A4090P | INEOS Olefins & Polymers Europe | HDPE Copolymer | Eltex® |
| Hostacom TKS708D | LyondellBasell Industries | TPO (POE) | Hostacom |
| INNOPOL® PE CS 5-8250 W | Inno-Comp Ltd. | HDPE | INNOPOL® PE |