GLS Nylon 6 PN09(E)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | GLS Polymers Pvt. Ltd. |
| Trademark: | GLS Nylon 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RpXV0r_GLS-Nylon-6-PN09-E-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon6 Precolor |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 to 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.3 to 1.8 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | > 60.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield) | > 4.0 | % | ASTM D638 |
| Flexural Modulus 3 | > 1500 | MPa | ASTM D790 |
| Flexural Strength 4 | > 78.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | > 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | > 150 | °C | |
| 1.8 MPa, Unannealed | > 58.0 | °C | |
| Vicat Softening Temperature | > 210 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 55.0 to 95.0 | °C | |
| Injection Pressure | 70.0 to 105 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MEGOLON™ S501 | AlphaGary | TP, Unspecified | MEGOLON™ |
| Ad-Tech Epoxy EL-339 | Ad-Tech Plastic Systems Corp. | Epoxy | Ad-Tech Epoxy |
| Fiberfil® J-60/40/E/EX | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Karina CLEAR PVC COMPOUND 65/200 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ VERTON™ PX91200 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ VERTON™ |