Rilsan® HT CESV BLACK P123 TL
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® HT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F2IX7d_Rilsan-HT-CESV-BLACK-P123-TL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® HT CESV BLACK P123 TL is a flexible polyphthalamide produced from a renewable source, typically used to replace metal in tubing for high temperature and/or demanding technical applications such as requiring high hydrolysis resistance. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 1.21 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 73 | ||
| Shore D, 15 sec | 68 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1150 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 36.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 130 | % | ISO 527-2 |
| Flexural Modulus | 1100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 18 | kJ/m² | |
| 23°C | 73 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 103 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 81.0 | °C | ISO 75-2/A |
| Melting Temperature | 270 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hoop Stress | |||
| 23°C | 34.0 | MPa | |
| 150°C | 6.90 | MPa | |
| Renewable Carbon Conent | 45 | % | ASTM D6866 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 8.0 | hr | |
| Melt Temperature | 270 to 300 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 2607 | Covestro - Polycarbonates | PC | Makrolon® |
| Sinvicomp SFC8210 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| TOTAL Polyethylene EVA 1003 VN 4 | TOTAL Refining & Chemicals | EVA | TOTAL Polyethylene |
| Karina BEIGE COLOR CONCENTRATE -E 08/244-RG-GE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8215-60 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |