AIE PA6 50G4F

Category: Nylon 6 , Polyamide 6
Manufacturer: Asia International Enterprise (Hong Kong) Limited
Trademark: AIE PA6
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: Rk7Kta_AIE-PA6-50G4F.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
AIE PA6 50G4F is a Polyamide 6 (Nylon 6) material filled with 20% glass fabric. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding.

Important attributes of AIE PA6 50G4F are:
  • Flame Rated
  • Flame Retardant
  • Heat Resistant
General Information
Filler / Reinforcement
  • Glass Fabric, 20% Filler by Weight
Features
  • Flame Retardant
  • High Heat Resistance
Forms
  • Pellets
Processing Method
  • Injection Molding
PhysicalNominal ValueUnitTest Method
Density 1.52g/cm³ISO 1183
Molding Shrinkage 0.40 to 0.80%Internal Method
Water Absorption (23°C, 24 hr)1.6%ISO 62
MechanicalNominal ValueUnitTest Method
Tensile Stress (Yield)142MPaISO 527-2
Tensile Strain (Break)3.0%ISO 527-2
Flexural Modulus 7500MPaISO 178
Flexural Stress 210MPaISO 178
ImpactNominal ValueUnitTest Method
Notched Izod Impact Strength (23°C)18kJ/m²ISO 180
ThermalNominal ValueUnitTest Method
Heat Deflection Temperature
    0.45 MPa, Unannealed 210°CISO 75-2/B
    1.8 MPa, Unannealed 202°CISO 75-2/A
Melting Temperature (DSC) 225°CISO 3146
FlammabilityNominal ValueTest Method
Flame Rating (1.50 mm)V-0UL 94
InjectionNominal ValueUnit
Drying Temperature 90.0 to 100°C
Drying Time 2.0 to 4.0hr
Processing (Melt) Temp 220 to 250°C
Mold Temperature 50.0 to 100°C
Injection Pressure 30.0 to 80.0MPa
Resin Grade Manufacturer Category Trademark
Quadrant EPP Semitron® ESd 420 V Quadrant Engineering Plastic Products PEI Quadrant EPP
TAFMER™ A-35070S Mitsui Chemicals America, Inc. PAO TAFMER™
Torayca® NX85K-15 Toray Resin Company PC Torayca®
HYBRAR™ 5127 Kuraray Co., Ltd. TPE HYBRAR™
Clear-Flex® FG 106 A Versalis S.p.A. LLDPE Clear-Flex®