LubriOne™ LB3100-8008 HS GR001
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | PolyOne Corporation |
| Trademark: | LubriOne™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k0wcLr_LubriOne-LB3100-8008-HS-GR001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LubriOne™Lubricating and wear-resistant polymers are specially used for self-lubricating materials, and their friction coefficient is low, which can improve wear resistance. LubriOne polymers have been proven to reduce friction, noise, vibration, heat generation and improve product durability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 - 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 23°C) | 55.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | > 20 | % | ASTM D638 |
| Flexural Modulus 3(23°C) | 2300 | MPa | ASTM D790 |
| Flexural Strength 4(23°C) | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 400 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 106 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 80.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3660T | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| SUNPRENE® FE70DH | Mitsubishi Chemical Performance Polymers, Inc. | PVC Elastomer | SUNPRENE® |
| CoolPoly® D8102 | Celanese Corporation | TPE | CoolPoly® |
| DOMAMID® A1-509-I1-N | DOMO Engineering Plastics GmbH | Nylon 6 | DOMAMID® |
| Elastron® D D400.A35.T | Elastron USA, Inc. | SBS | Elastron® D |