Karina IVORY PVC COMPOUND 900-35/ 1-AYR-AC-LMP
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RgAg0s_Karina-IVORY-PVC-COMPOUND-900-35-1-AYR-AC-LMP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FLAME RETARDANT AND LEAD FREE PVC COMPOUND, FLEXIBLE AT LOW TEMPERATURES. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.29 to 1.35 | g/cm³ | ASTM D792 |
| Cadmium Content | < 50 | ppm | IEC 62321 |
| Chromium Content | < 100 | ppm | IEC 62321 |
| Color | OK | ME 12 | |
| Color a | -2.07 to 0.930 | ME 12 | |
| Color b | 2.02 to 5.02 | ME 12 | |
| Color L | 91.9 to 94.9 | ME 12 | |
| Mercury Content | < 100 | ppm | IEC 62321 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bromine Content | < 100 | ppm | IEC 62321 |
| Lead Content | < 100 | ppm | IEC 62321 |
| Maximum Variation of Elongation | < 25 | % | ASTM D638 |
| Maximum Variation of Tensile Strength | < 25 | % | ASTM D638 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 88 to 92 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | > 12.6 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 150 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 12.6 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | > 150 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -25.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 1.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | > 30 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged in Air for 168 hr at 136°C |
| 3 . | Aged in Air for 168 hr at 136°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PVC Film 06-A0370R-87NT | Teknor Apex Company | PVC, Flexible | PVC Film |
| Badaflex® TPE-S 50A 1000LD | Bada AG | TPE | Badaflex® |
| CERTENE™ LDI-2523 | Muehlstein | LDPE | CERTENE™ |
| KOPA® KN333G30CR | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| Karina CLEAR PVC COMPOUND -E 85/243-DA-AT-IS-SI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |