Ultramid® T KR 4357 G6
| Category: | Nylon 6/6T , Polyamide 6/6T Copolymer |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RTxRtz_Ultramid-T-KR-4357-G6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultramid T KR 4357 is a 30% glass fiber reinforced, impact-modified, injection-molding PA6/6T grade. High toughness, stiffness and strength, low water absorption. High melting point (295 C). After the material has been conditioned, its mechanical properties remain stable up to 60 C. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.37 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 4.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.80 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9300 | 9000 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Break, -40°C | 249 | 235 | MPa | |
| Break, 23°C | 165 | 145 | MPa | |
| Tensile Strain (Break, 23°C) | 3.5 | 3.5 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 10 | -- | kJ/m² | |
| 23°C | 19 | 21 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 90 | -- | kJ/m² | |
| 23°C | 95 | 100 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 23 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 270 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 295 | -- | °C | ISO 3146 |
| CLTE | ||||
| Flow | 2.5E-5 | -- | cm/cm/°C | |
| Transverse | 5.5E-5 | -- | cm/cm/°C | |
| RTI Elec | UL 746 | |||
| 0.750 mm | 140 | -- | °C | |
| 1.50 mm | 140 | -- | °C | |
| 3.00 mm | 140 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.750 mm | 100 | -- | °C | |
| 1.50 mm | 110 | -- | °C | |
| 3.00 mm | 115 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.750 mm | 120 | -- | °C | |
| 1.50 mm | 140 | -- | °C | |
| 3.00 mm | 140 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 4.30 | 4.50 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.030 | 0.040 | IEC 60250 | |
| Comparative Tracking Index | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ResMart Ultra HoPP 20 | ResMart | PP Homopolymer | ResMart Ultra |
| TAIRIPRO K7005 | Formosa Plastics Corporation | PP Impact Copolymer | TAIRIPRO |
| GATONE™ 5300PF | Solvay Specialities India Private Limited (SSIPL) | PEEK | GATONE™ |
| EcoPaXX® Q-X07207 | DSM Engineering Plastics | Nylon 410 | EcoPaXX® |
| INNOPOL® PP CS 2-2120 | Inno-Comp Ltd. | PP Copolymer | INNOPOL® PP |