Order Products : sales@su-jiao.com
TEKAMID™ HT14ST
| Category: | Nylon 6+ABS , Polyamide 6 + ABS |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | TEKAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RM2aEK_TEKAMID-HT14ST.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| H14ST is a unreinforced PA6/ABS alloy product with super toughness. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.90 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 47.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 100 | % | ASTM D638 |
| Flexural Modulus 3 | 1960 | MPa | ASTM D790 |
| Flexural Strength 4 | 73.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.18 mm | > 390 | J/m | ASTM D256 |
| 23°C, 3.18 mm 5 | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 80.0 | °C | ASTM D648 |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 120 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 230 - 250 | °C | |
| Middle Temperature | 230 - 250 | °C | |
| Front Temperature | 230 - 250 | °C | |
| Nozzle Temperature | 240 - 260 | °C | |
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 70.0 - 90.0 | °C |
| Injection instructions |
|---|
| Injection Speed: 30 to 70%Injection Pressure - 1st: 20 to 50%Injection Pressure - 2nd: 20 to 50%Injection Pressure - Back Pressure: 0 to 20% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| 5 . | 90 kgf-cm/cm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN AX4000 | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| Network Polymers PP PPB 25 2010 | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| CALP MRP440 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| DENYL HT 6010 | Vamp Tech | PPA | DENYL |
| LUVOCOM® 80-7555 VP | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |