LNP™ LUBRICOMP™ CZL36 compound
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RLxCwZ_LNP-LUBRICOMP-CZL36-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* CZL36 is a compound based on Polystyrene resin containing 30% Milled Glass and 15% PTFE. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound PDX-C-01818 Product reorder name: CZL36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 to 0.30 | % | ASTM D955 |
| Across Flow : 24 hr | 0.30 to 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.31 to 0.37 | % | ISO 294-4 |
| Flow : 24 hr | 0.24 to 0.26 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.030 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.090 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2550 | MPa | ASTM D638 |
| -- | 3880 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 24.6 | MPa | ASTM D638 |
| Yield | 22.0 | MPa | ISO 527-2 |
| Break | 24.2 | MPa | ASTM D638 |
| Break | 21.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 1.7 | % | ASTM D638 |
| Yield | 1.6 | % | ISO 527-2 |
| Break | 2.3 | % | ASTM D638 |
| Break | 3.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 4900 | MPa | ASTM D790 |
| -- | 5120 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 52.0 | MPa | ASTM D790 |
| -- | 49.4 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 27 | J/m | ASTM D256 |
| 23°C 2 | 2.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 120 | J/m | ASTM D4812 |
| 23°C 3 | 7.8 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 2.90 | J | ASTM D3763 |
| -- | 0.890 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 83.3 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 83.0 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 6.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Transverse : -40 to 40°C | 6.7E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 6.8E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 249 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax 6331NW | LyondellBasell Industries | PP Homopolymer | Pro-fax |
| Vital-Line SHE8595G | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| CYROLITE® CG-97 | Evonik Cyro LLC | Acrylic (PMMA) | CYROLITE® |
| Evoprene™ GF 6255 | AlphaGary | SBC | Evoprene™ GF |
| LNP™ LUBRICOMP™ KP002 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |