EPIMIX PBT/PET GV0 30 NC
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | EPSAN Plastik SAN. ve TiC. A.S. |
| Trademark: | EPIMIX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R5KE25_EPIMIX-PBT-PET-GV0-30-NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EPIMIX PBT/PET , Flame retardant, reinforced with 30% of glass fiber, heat stabilized, lubricated for injection moulding. EPIMIX PBT/PET GV0 30 ,Halogenated , is used in all sectors of industry , compliance with RoHs derivatives, with rating UL94 V0 , offering a perfect balance of thermal and mechanical properties. This product is available in natural and in colours on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.72 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 3.00mm | 1.0 | -- | % | ISO 294-4 |
| Flow direction : 3.00mm | 0.30 | -- | % | ISO 294-4 |
| Moisture Content | 0.20 | -- | % | ISO 15512 |
| Ash Content | 30 | -- | % | ISO 3451-4 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 84 | -- | ISO 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 11500 | 10000 | MPa | ISO 527-2/50 |
| Tensile Stress (Break, 23°C) | 135 | 100 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 2.0 | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 9750 | 9000 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 195 | 180 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | 9.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 7.0 | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 3 | ||||
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 200 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | -- | °C | ISO 306/B120 |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 250 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | -- | UL 94, IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index (0.800 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Additional Information |
|---|
| 干燥 TEST CONDITIONS: Laboratory conditions are 23 ±2°C and 45-55 % RH. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 260 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SKYBOND® 703 | Industrial Summit Technology Co. | API | SKYBOND® |
| StarFlex P 7335-9000 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | Starflex |
| Witcom PA12 2010/039 | Witcom Engineering Plastics B.V. | Nylon 12 | Witcom PA12 |
| ELASTOSIL® 5000 | Wacker Chemie AG | Silicone | ELASTOSIL® |
| Lucopren® SE 1522-75FS | Lucobit AG | SEPS | Lucopren® |