VALOX™ 830F resin
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Qvu6S7_VALOX-830F-resin-89195.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT+PET, 30% Glass, Mold Release, Heat Stabilized, For foodcontact applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.54 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (265°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 to 0.80 | % | Internal Method |
| Water Absorption | ASTM D570, ISO 62 | ||
| Saturation, 23°C | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.060 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8000 | MPa | ASTM D638 |
| -- | 9000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 100 | MPa | ASTM D638 |
| Yield | 140 | MPa | ISO 527-2/5 |
| Break 3 | 105 | MPa | ASTM D638 |
| Break | 140 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.5 | % | ASTM D638 |
| Yield | 2.5 | % | ISO 527-2/5 |
| Break 5 | 2.5 | % | ASTM D638 |
| Break | 2.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 7000 | MPa | ASTM D790 |
| -- 7 | 8000 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 200 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 170 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 70 | J/m | ASTM D256 |
| 23°C | 80 | J/m | ASTM D256 |
| -30°C 10 | 8.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 9.0 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 7.00 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 195 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 12 | 202 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 200 | °C | ASTM D1525, ISO 306/B50 10 13 |
| -- | 205 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 40°C | 2.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 8.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 80°C | 8.1E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 240 to 260 | °C | |
| Middle Temperature | 255 to 280 | °C | |
| Front Temperature | 260 to 280 | °C | |
| Nozzle Temperature | 265 to 275 | °C | |
| Processing (Melt) Temp | 260 to 285 | °C | |
| Mold Temperature | 60.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 120*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| megol® WR 70 | API SpA | SEBS | megol® |
| SORVEX 900 | Sorensen Ventures | PBT | SORVEX |
| EverGlide® MB3950 | Polymer Dynamix | EVA | EverGlide® |
| PermaStat® 100 MD | RTP Company | PP, Unspecified | PermaStat® |
| Sylvin 2990-93 Green 3170 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |