POLYAXIS® LP 624
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | A. Schulman Inc. |
| Trademark: | POLYAXIS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HhIbdg_POLYAXIS-LP-624.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Long term UV8 stabilization |
| General Information | |
|---|---|
| Additive |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 0.942 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (100% Igepal, Compression Molded, F50) | > 500 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield, Rotational Molded) | 17.9 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Rotational Molded) | 400 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Rotational Molded) | 124 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength (-40°C, 3.18 mm, Rotational Molded) | 65 | J | ARM |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Rotational Molded) | 55.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (Any Color) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Compression Molded |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVASTER® B1 GF 6 | Plastcom | PBT | SLOVASTER® |
| Styrolux® 3G46 | INEOS Styrolution Group GmbH | SBC | Styrolux® |
| ALCOM® PC 740/4 GY1262-05LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| Catalyst CT/1-LR UV | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |
| MAJORIS FFR037 - 1298 | AD majoris | PP, Unspecified | MAJORIS |