XENOY™ CL101 resin
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | XENOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Qu90k8_XENOY-CL101-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Xenoy CL101 is an unfilled, impact modified PC/PBT blend with excellent solvent resistance and low-temperature ductility. It has a proven track record in off-line painted exterior automotive applications. ISO1043: PC+PBT-I. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 14 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | Internal Method | ||
| Flow | 0.70 to 1.1 | % | |
| Across Flow | 0.70 to 1.1 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.50 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 89 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 82.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2050 | MPa | ASTM D638 |
| -- | 2050 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 53.0 | MPa | ASTM D638 |
| Yield | 52.0 | MPa | ISO 527-2/50 |
| Break 4 | 49.0 | MPa | ASTM D638 |
| Break | 44.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 5 | 4.5 | % | ASTM D638 |
| Yield | 4.5 | % | ISO 527-2/50 |
| Break 6 | 50 | % | ASTM D638 |
| Break | 50 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 7 | 2000 | MPa | ASTM D790 |
| -- 8 | 2000 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 75.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 9 | 75.0 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 30.0 | mg | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C 10 | 25 | kJ/m² | ISO 179/1eA |
| -30°C | 20 | kJ/m² | ISO 179/2C |
| -20°C | 25 | kJ/m² | ISO 179/2C |
| 23°C 11 | 58 | kJ/m² | ISO 179/1eA |
| 23°C | 30 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength 12 | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| -30°C | 450 | J/m | ASTM D256 |
| 0°C | 600 | J/m | ASTM D256 |
| 23°C | 630 | J/m | ASTM D256 |
| -40°C 13 | 25 | kJ/m² | ISO 180/1A |
| -30°C 14 | 35 | kJ/m² | ISO 180/1A |
| 23°C 15 | 50 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 16 | ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 100 mm Span 17 | 105 | °C | ISO 75-2/Be |
| 0.45 MPa, Unannealed, 64.0 mm Span 18 | 105 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 83.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 19 | 83.0 | °C | ISO 75-2/Ae |
| 1.8 MPa, Unannealed, 64.0 mm Span 20 | 83.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 120 | °C | ASTM D1525, ISO 306/B50 12 21 |
| -- | 155 | °C | ISO 306/A50 |
| -- | 123 | °C | ISO 306/B120 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 40°C | 9.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 9.5E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 80°C | 9.5E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.18 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| 1.00 mm 22 | 18 | kV/mm | |
| 3.20 mm, in Oil | 17 | kV/mm | |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 3.30 | ||
| 60 Hz | 3.30 | ||
| 1 MHz | 3.30 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 2.0E-3 | ||
| 60 Hz | 2.0E-3 | ||
| 1 MHz | 0.020 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 230 to 250 | °C | |
| Middle Temperature | 240 to 265 | °C | |
| Front Temperature | 250 to 270 | °C | |
| Nozzle Temperature | 250 to 265 | °C | |
| Processing (Melt) Temp | 255 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | Type I, 50 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*4 sp=62mm |
| 12 . | 80*10*4 sp=62mm |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 |
| 16 . | 80*10*4 |
| 17 . | 120*10*4 mm |
| 18 . | 80*10*4 mm |
| 19 . | 120*10*4 mm |
| 20 . | 80*10*4 mm |
| 21 . | Rate B (120°C/h), Loading 2 (50 N) |
| 22 . | Short-Time |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer SFX-19250BM | Shin-Etsu Silicones of America | Fluoro Si | Shin-Etsu Elastomer |
| Shuman PC 980-05V0 | Shuman Plastics, Inc. | PC | Shuman PC |
| Unichem 92-623A | Colorite Polymers | PVC, Unspecified | Unichem |
| BONDYRAM® TL1306 | Polyram Ram-On Industries | PP, Unspecified | BONDYRAM® |
| Ecomann® PHA EM80000 | Shenzhen Ecomann Biotechnology Co., Ltd. | PHA | Ecomann® |