China PPS PTFE-hGR303
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Sichuan Deyang Chemical Co., Ltd |
| Trademark: | China PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t7it8G_China-PPS-PTFE-hGR303.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PPS/PTFE-hGR303 is lubricant PPS compound, which is filled with glass fiber, PTFE and ingredients based on the PPS resin. It shows abrasive resistance, solvent resistance and good mechanic prosperity, high modulus, creep resistance, high-temperature resistance, inherent flame resistance, easy processing, low mold shrinkage. Owing to its high performance, it's widely used in mechanical and chemical industry for making structures and wearing pieces in the condition of high temperature, high pressure and corrosive solvent. It's also an excellent candidate in aerospace field. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.62 | g/cm³ | Internal method |
| Ash Content | 34 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion - Width | 6 | mm | Internal method |
| Abrasion Loss 1 | 2.0 | mg | Internal method |
| Tensile Strength | 137 | MPa | Internal method |
| Flexural Modulus | 12000 | MPa | Internal method |
| Flexural Strength | 202 | MPa | Internal method |
| Coefficient of Friction | 0.37 | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 15 | kJ/m² | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 263 | °C | Internal method |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 140 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 300 - 320 | °C | |
| Front Temperature | 300 - 320 | °C | |
| Nozzle Temperature | 290 - 320 | °C | |
| Processing (Melt) Temp | 160 - 180 | °C | |
| Mold Temperature | 100 - 150 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Back Pressure | 0.100 - 1.00 | MPa | |
| Screw Speed | 40 - 100 | rpm |
| Injection instructions |
|---|
| Processing time: 6 to 12hr |
| Note Message | |
|---|---|
| 1 . | 120 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® BGV HZ 15 Black | Radici Plastics | Nylon 6 | Radilon® |
| Ad-Tech Urethanes UC-4750 | Ad-Tech Plastic Systems Corp. | TSU | Ad-Tech Urethanes |
| Altuglas® MI-7T | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| DENYL HT 2010 | Vamp Tech | PPA | DENYL |
| Geon™ Vinyl Rigid Extrusion L0111 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |