Latigray 52/11-01 CX/70
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latigray |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Qs3Rc8_Latigray-52-11-01-CX-70.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Radiopaque compound based on Polypropylene homopolymer (PPh). Special mineral filler. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.97 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.0 to 1.5 | % | |
| Flow : 2.00 mm | 1.0 to 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 20.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 1.2 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.3 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 115 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 140 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 to 240 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 204A HS UV | RTP Company | Nylon 6 | RTP |
| Prime Impax 250 | Primex Plastics Corporation | PS (HIPS) | Prime Impax |
| TOYOBO PPS TS301 | TOYOBO America, Inc. | PPS | TOYOBO PPS |
| CP PRYME® Nylon 6 N100LZ NAT | Chase Plastics Services Inc. | Nylon 6 | CP PRYME® Nylon 6 |
| Flontech® FT-BRR55-M5-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |