Ferro PP TPP21AN89HB NATURAL
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | Ferro PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ql6tZs_Ferro-PP-TPP21AN89HB-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ferro PP TPP21AN89HB NATURAL is a Polypropylene Homopolymer (PP Homopolymer) material filled with 21% talc. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Primary attribute of Ferro PP TPP21AN89HB NATURAL: Homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.4 | % | |
| Across Flow | 1.6 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 22.4 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 35 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : 23°C | 1620 | MPa | |
| Tangent : 23°C | 1830 | MPa | |
| Flexural Strength (23°C) | 33.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 75 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 590 | J/m | ASTM D4812 |
| Gardner Impact (23°C) | 8.47 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 110 | °C | |
| 1.8 MPa, Unannealed | 62.8 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PREMIER™ A240-HTHF | Chomerics, div. of Parker Hannifin Corp. | PC+ABS | PREMIER™ |
| Daelim Po1y® LH-5540 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Formolon® 622W | Formosa Plastics Corporation, U.S.A. | PVC Homopolymer | Formolon® |
| Lupox® GP2306F | LG Chem Ltd. | PBT | Lupox® |
| MARPOL® Homo 7.0 | Marco Polo International, Inc. | PP Homopolymer | MARPOL® Homo |