Staramide PF007IX2
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Staramide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G4Odtr_Staramide-PF007IX2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Staramide PF0007IX2 is an Impact Modified Glass Fiber Reinforced Polyamide 6 Injection Molding Resin (also known as Star X 2010 33V) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (4.00 mm) | 0.20 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8700 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 125 | MPa | |
| Break | 123 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 2.9 | % | |
| Break | 3.0 | % | |
| Flexural Modulus 1 | 6800 | MPa | ISO 178 |
| Flexural Stress | 171 | MPa | ISO 178 |
| Flexural Strain at Break 2 | 4.0 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 20 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 55 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 217 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 200 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.7E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.2E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 240 to 250 | °C | |
| Middle Temperature | 250 to 260 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Processing (Melt) Temp | 250 to 260 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® B3EG4 | BASF Corporation | Nylon 6 | Ultramid® |
| NEFTEKHIM PP 4340N (EP2X49GA) | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Axiall PVC 8150 White 209 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| HAIPLEN H10 T6 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| KRITILEN® Masterbatches | PLASTIKA KRITIS S.A. | Unspecified | KRITILEN® |