LNP™ VERTON™ E9007E compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QguPPh_LNP-VERTON-E9007E-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON E9007E is a compound based on Polyetherimide (PEI) containing 35% Long Carbon Fiber. Added features of this grade include: Structural, High Temperature Also known as: LNP* VERTON* Compound E9007E Product reorder name: E9007E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 32000 | MPa | ASTM D638 |
| -- | 33000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 267 | MPa | ASTM D638 |
| Break | 253 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.0 | % | ASTM D638 |
| Break | 0.90 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 28900 | MPa | ASTM D790 |
| -- 5 | 28500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 411 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 429 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 170 | J/m | ASTM D256 |
| 23°C 7 | 16 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 520 | J/m | ASTM D4812 |
| 23°C 8 | 34 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 9(1.8 MPa, Unannealed, 64.0 mm Span) | 215 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 8.0E-6 | cm/cm/°C | |
| Transverse : -30 to 30°C | 2.2E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 343 to 370 | °C | |
| Middle Temperature | 350 to 380 | °C | |
| Front Temperature | 350 to 380 | °C | |
| Processing (Melt) Temp | 350 to 380 | °C | |
| Mold Temperature | 175 to 200 | °C | |
| Back Pressure | 0.290 to 0.430 | MPa | |
| Screw Speed | 20 to 40 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Teslin® SPID 1000 | PPG Industries, Inc. | PE, Unspecified | Teslin® |
| Akulon® Ultraflow K-FLG6/E | DSM Engineering Plastics | Nylon 6 | Akulon® Ultraflow |
| Jam HDPE HF7740F2 | Jam Petrochemical Company | HDPE | Jam HDPE |
| Pearlthane® ECO D12T85 | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Pearlthane® ECO |
| Plaslube® POM HO CF10 TL20 | Techmer Engineered Solutions | Acetal (POM) Homopolymer | Plaslube® |