NEFTEKHIM PP 4210G (EP2S30B)
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Nizhnekamskneftekhim Inc. |
| Trademark: | NEFTEKHIM PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Qdgb1c_NEFTEKHIM-PP-4210G-EP2S30B-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product obtained by copolymerization of propylene and ethylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, higher thermal-oxidative degradation resistance when PP is produced, processed and PP-made articles are exploited. Application: extrusion of sheets, blow molding, tubular film. Technical requirements: TU 2211-136-05766801-2006 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | |
| Apparent Density | 0.48 to 0.60 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.5 to 2.0 | g/10 min | ASTM D1238 |
| Ash Content | 0.025 to 0.050 | % | |
| Gel Content 1 | |||
| > 200.0 µm | 300 | pcs/m² | |
| 0.700 to 1.50 mm | 3.00 | pcs/m² | |
| 1.50 to 2.50 mm | 0.00 | pcs/m² | |
| > 2.50 mm | 0.00 | pcs/m² |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Thermal Creep Temperature 2 | 70 to 80 | °C | |
| Thermal-oxidative Deterioration (150°C) | 20.8 | day |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 75 to 82 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 26.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 11 | % | ASTM D638 |
| Flexural Modulus | 900 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 90 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Vicat Softening Temperature 3 | 130 to 138 | °C |
| Note Message | |
|---|---|
| 1 . | p.4.8 TU 2211-136-05766801-2006 |
| 2 . | at load 0.46 H/mm² |
| 3 . | in liquid medium under force 10 H |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecnoprene® HKM41 D NAT003 | SO.F.TER. SPA | PP Homopolymer | Tecnoprene® |
| TEKAPPO™ JF2 | Mando Advanced Materials Co., Ltd. | PPE+PS | TEKAPPO™ |
| Nypol® PA A3 G25 PRTA010 NR438 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Karina GRAY PVC COMPOUND 853-18/233-DY-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Badatron® PPS CF40 | Bada AG | PPS | Badatron® |