Nymax™ GF 600 A 33 Black 28 V
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Nymax™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QIbGQI_Nymax-GF-600-A-33-Black-28-V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nymaxm of glass fiber reinforced nylon 6 polymer®GF600 series products are specially designed for high rigidity, tensile strength and toughness applications, and their surface appearance is improved compared with nylon 6/6 polymer. According to the required stiffness characteristics, these materials have a variety of strength levels to choose from and are easy to process in most standard thermoplastic processing equipment. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.0E-3 - 3.0E-3 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.2 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Fracture 1 | 152 | MPa | ASTM D638 |
| Fracture | 154 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield 2 | 3.0 | % | ASTM D638 |
| Yield | 2.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 8270 | MPa | ASTM D790 |
| -- | 8900 | MPa | ISO 178 |
| Flexural Strength | 221 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, 3.18mm, injection molding | 80 | J/m | ASTM D256A |
| -- | 10 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, annealed, 3.18mm | 200 | °C | ASTM D648 |
| 1.8 MPa, annealed | 204 | °C | ISO 75-2/A |
| Additional Information |
|---|
| Molded Test Bars: Dry as Molded |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Mold Temperature | 48.9 - 93.3 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1382 D TFE 5 | RTP Company | PPS | RTP |
| Royalene® 580HT | Lion Copolymer, LLC | EPDM | Royalene® |
| Fainplast PVC ART 0665/S | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Hifax HSBM CB 1151 G | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| Hanwha Total PE R908U | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | HDPE | Hanwha Total PE |