Pro-fax 7823
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Pro-fax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KxConh_Pro-fax-7823.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pro-fax 7823 fractional melt flow polypropylene copolymer is available in pellet form. This resin is typically used in extrusion applications and offers high melt strength and excellent impact resistance. An ASTM and ISO-based versions of the technical datasheet are available for Pro-fax 7823 For regulatory compliance information see Pro-fax 7823 Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.898 | g/cm³ | ASTM D792B |
| -- | 0.900 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.45 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 28.0 | MPa | ASTM D638 |
| Yield, 23°C | 26.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 11 | % | ASTM D638 |
| Yield, 23°C | 11 | % | ISO 527-2 |
| Flexural Modulus | |||
| 1% Secant 2 | 1240 | MPa | ASTM D790A |
| 23°C | 1180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 2.9 | kJ/m² | |
| 23°C | 66 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C | No Break | ASTM D256A | |
| -40°C | 4.0 | kJ/m² | ISO 180 |
| 23°C | 64 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 85.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 78.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 49.0 | °C | ISO 75-2/A |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3507 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| LNP™ LUBRILOY™ A3000XXP compound | SABIC Innovative Plastics Europe | ABS | LNP™ LUBRILOY™ |
| LNP™ THERMOCOMP™ UC006XXH compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |
| Capilene® CT 80 A | Carmel Olefins Ltd. | PP Random Copolymer | Capilene® |
| Hostacom XBR 169 G C13036 | LyondellBasell Industries | PP Copolymer | Hostacom |