NEFTEKHIM PP 5213M (RCXP723)
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Nizhnekamskneftekhim Inc. |
| Trademark: | NEFTEKHIM PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QCH8Z0_NEFTEKHIM-PP-5213M-RCXP723-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product obtained by copolymerization of propylene and ethylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation resistance when PP is produced, processed and PP-made articles are exploited, improved properties preventing from film layers sticking. Application: flat-slot extrusion metallized film. Technical requirements: TU 2211-136-05766801-2006 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | |
| Apparent Density | 0.48 to 0.60 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 to 12 | g/10 min | ASTM D1238 |
| Ash Content | 0.025 to 0.050 | % | |
| Gel Content 1 | |||
| > 200.0 µm | 300 | pcs/m² | |
| 500.0 to 700.0 µm | 3.00 | pcs/m² | |
| 0.700 to 1.50 mm | 0.00 | pcs/m² | |
| 1.50 to 2.50 mm | 0.00 | pcs/m² |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Thermal Creep Temperature 2 | 70 to 80 | °C | |
| Thermal-oxidative Deterioration (150°C) | 6.3 | day |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 75 to 82 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 27.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 10 | % | ASTM D638 |
| Flexural Modulus | 950 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Vicat Softening Temperature 3 | 130 to 138 | °C |
| Note Message | |
|---|---|
| 1 . | p.4.8 TU 2211-136-05766801-2006 |
| 2 . | at load 0.46 H/mm² |
| 3 . | in liquid medium under force 10 H |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bynel® 41E710 | DuPont Packaging & Industrial Polymers | LLDPE | Bynel® |
| Huafon HF-1071D | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |
| Hytrel® G4074 | DuPont Performance Polymers | TPC-ET | Hytrel® |
| Kazan HDPE 293-2B5D | Kazanorgsintez Joint Stock Company | HDPE | Kazan HDPE |
| POLYCASA® XT Soft Tone | Polycasa | Acrylic (PMMA) | POLYCASA® |