Nymax™ GF 1200 A 55 HS Black 13
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Nymax™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Pu4g83_Nymax-GF-1200-A-55-HS-Black-13.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nymax of nylon 6/6 polymers reinforced with glass fibers®GF 1200 series products are specially used in harsh environments and have the characteristics of high rigidity, tensile properties, heat resistance, durability, etc. According to the needs of rigid characteristics, these materials have a large range of strength and are easy to process in standard thermoplastic processing equipment. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.64 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 - 0.30 | % | ASTM D955 |
| Water Absorption (24 hr, 3.18 mm) | 0.60 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Fracture 1 | 221 | MPa | ASTM D638 |
| -- 2 | 209 | MPa | ISO 527 |
| Tensile Elongation 3(Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | |||
| -- 4 | 16200 | MPa | ISO 178 |
| -- | 15200 | MPa | ASTM D790 |
| Flexural Strength | 310 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, 3.18mm, injection molding | 91 | J/m | ASTM D256A |
| -- | 11 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.18mm | 257 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 248 | °C | ISO 75-2 |
| 1.8 MPa, unannealed, 3.18mm | 248 | °C | ASTM D648 |
| Additional Information |
|---|
| 模制试验条：模制时干燥 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Mold Temperature | 60.0 - 107 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | Type 1, 5.1 mm/min |
| 4 . | 25 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DESLOY™ DSC892C | DESCO Co., Ltd. | PC+ABS | DESLOY™ |
| Kotex KV-30FD | Kotec Corporation | PC | Kotex |
| Karina GREEN COLOCOR CONCENTRATE 40/ 21-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TECACOMP® PA66 GF30 TF15 HI black 3366 | Ensinger GmbH | Nylon 66 | TECACOMP® |
| Kepital® ES-20 | KEP Americas | Acetal (POM) Copolymer | Kepital® |