KRALASTIC® MM
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Nippon A&L Inc. |
| Trademark: | KRALASTIC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eWDfHe_KRALASTIC-MM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KRALASTIC®MM is an acrylonitrile butadiene styrene (ABS) material,. This product is available in North America or Asia Pacific region. The processing method is injection molding. KRALASTIC®The main features of MM are:
|
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.06 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 4.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.40 - 0.60 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 119 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 59.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 2750 | MPa | ISO 178 |
| Flexural Stress (23°C) | 91.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 84.0 | °C | ISO 75-2/A |
| CLTE - Flow (23 to 80°C) | 7.3E-5 | cm/cm/°C | JIS K7197 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Ball Pressure Registration Temperature: 90°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | > 3.0 | hr | |
| Rear Temperature | 200 - 260 | °C | |
| Middle Temperature | 200 - 260 | °C | |
| Front Temperature | 200 - 260 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren Y1200 (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| TOPAS® 8007S-04 | Topas Advanced Polymers, Inc. | COC | TOPAS® |
| AKROMID® A3 GF 25 1 L black (4672) | AKRO-PLASTIC GmbH | Nylon 66+PP | AKROMID® |
| CERTENE™ SIM-080 | Muehlstein | PS (HIPS) | CERTENE™ |
| Karina CREPE PVC COMPOUND 870-22/70-A-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |