Stratasys PC
| Category: | PC , Polycarbonate |
| Manufacturer: | Stratasys |
| Trademark: | Stratasys |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PgllVG_Stratasys-PC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Production-Grade Thermoplastic for Fortus 3D Production Systems A true industrial thermoplastic, PC (polycarbonate) is widely used in automotive, aerospace, medical and many other applications. PC offers accuracy, durability and stability, creating strong parts that withstand functional testing. A PC part manufactured on a Fortus® 3D Production System is 5-60 percent stronger than a part made on previous FDM® systems. It also has superior mechanical properties to ABS and a number of other thermoplastics. When combined with a Fortus system, PC gives you Real Parts™ for conceptual modeling, functional prototyping, manufacturing tools, and end-use-parts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Thickness - Layer Capability | 127.0 to 330.2 | µm |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistance 1 | 6.0E+13 to 2.0E+14 | ohms | ASTM D257 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2(3.18 mm) | 2280 | MPa | ASTM D638 |
| Tensile Strength 3(3.18 mm) | 67.6 | MPa | ASTM D638 |
| Tensile Elongation 4(Break, 3.18 mm) | 5.0 | % | ASTM D638 |
| Flexural Modulus 5 | 2230 | MPa | ASTM D790 |
| Flexural Strength 6 | 104 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256A |
| Unnotched Izod Impact (23°C) | 320 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 138 | °C | |
| 1.8 MPa, Unannealed | 127 | °C | |
| Glass Transition Temperature | 161 | °C | DMA |
| Vicat Softening Temperature | 139 | °C | ASTM D1525 |
| CLTE - Flow | 6.8E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 14 to 15 | kV/mm | ASTM D149 |
| Dielectric Constant 7 | 2.80 to 3.00 | ASTM D150 | |
| Dissipation Factor 8 | 5.0E-4 to 6.0E-4 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly the result of the difference in properties of test plaques built in the flat vs. vertical orientation. |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Type I, 5.1 mm/min |
| 4 . | Type I, 5.1 mm/min |
| 5 . | Method I (3 point load), 1.3 mm/min |
| 6 . | Method I (3 point load), 1.3 mm/min |
| 7 . | All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly the result of the difference in properties of test plaques built in the flat vs. vertical orientation. |
| 8 . | All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly the result of the difference in properties of test plaques built in the flat vs. vertical orientation. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PBT GP1001S | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| Unichem 8024 | Colorite Polymers | PVC, Unspecified | Unichem |
| NOVAREX® 7022R | Mitsubishi Engineering-Plastics Corp | PC | NOVAREX® |
| LNP™ LUBRICOMP™ UFL36AS compound | SABIC Innovative Plastics | PPA | LNP™ LUBRICOMP™ |
| OnForce™ LFT PP-60LGF/001 Black UV | PolyOne Corporation | PP Homopolymer | OnForce™ LFT |