Sumitomo DAP 52-40-40-P
| Category: | DAP , Diallyl Phthalate |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | Sumitomo DAP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PeAsG8_Sumitomo-DAP-52-40-40-P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 52-40-40-P is a long glass fiber reinforced diallyl phthalate molding compound, which meets the requirements of ASTM D5948 Type GDI-30F. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.79 | g/cm³ | ASTM D792 |
| Apparent Density | 0.30 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.15 to 0.35 | % | ASTM D955 |
| Water Absorption - 48 hr (50°C) | 0.32 | % | ASTM D570 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability - Ignition | 1.5 | min | ASTM D229 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 13800 | MPa | ASTM D790 |
| Flexural Strength | 125 | MPa | ASTM D790 |
| Compressive Strength | 187 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 52 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed | 260 | °C | |
| 1.8 MPa, Annealed | > 280 | °C | |
| CLTE - Flow | 2.2E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.31 | W/m/K | ASTM C518 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | 17 | kV/mm | ASTM D149 |
| Dielectric Constant 2 | ASTM D150 | ||
| 1 kHz | 4.40 | ||
| 1 MHz | 4.30 | ||
| Dissipation Factor 3 | ASTM D150 | ||
| 1 kHz | 0.010 | ||
| 1 MHz | 0.016 | ||
| Arc Resistance | 133 | sec | ASTM D495 |
| Comparative Tracking Index | > 600 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 30 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | 60 Hz, Wet |
| 2 . | Wet |
| 3 . | Wet |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ASI POLYETHYLENE LP 554-01 | A. Schulman Inc. | HDPE | ASI POLYETHYLENE |
| Formolene® 6610A | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| DynaMix™ 3200-H | Polymer Dynamix | PEEK | DynaMix™ |
| INEOS HDPE T50-2000-119 | INEOS Olefins & Polymers USA | HDPE Copolymer | INEOS HDPE |
| LG ASA LI980G | LG Chem Ltd. | ASA | LG ASA |