| Fortron ICE 717F is a glass/mineral reinforced material with superior fuel resistance. It is specially designed to work in the environment of high temperature and high ethanol content. It offiers excellent physical properites similar to those of the Fortron standard glass/mineral reinforced products. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.98 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.18 - 0.23 | % | ISO 294-4 |
| Flow direction | 0.11 - 0.16 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.19 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 102 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 135 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.1 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 18500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 210 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.9 | kJ/m² | ISO 179/1eA |
| 23°C | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 24 | kJ/m² | ISO 179/1eU |
| 23°C | 22 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 5.6 | kJ/m² | ISO 180/1A |
| 23°C | 6.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 22 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, not annealed | 277 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 235 | °C | ISO 75-2/C |
| Glass Transition Temperature 1 | 90.0 | °C | ISO 11357-2 |
| Melting Temperature 2 | 280 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.6E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 - 140 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 290 - 300 | °C | |
| Middle Temperature | 310 - 320 | °C | |
| Front Temperature | 330 - 340 | °C | |
| Nozzle Temperature | 310 - 330 | °C | |
| Processing (Melt) Temp | 330 - 340 | °C | |
| Mold Temperature | 90.0 - 160 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 30.0 - 70.0 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 330 to 340°CZone 4 Temperature: 330 to 340°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zytel® 158 NC010 | DuPont Performance Polymers | Nylon 612 | Zytel® |
| NEFTEKHIM PS 680 | Nizhnekamskneftekhim Inc. | PS (HIPS) | NEFTEKHIM PS |
| OMIKRON HR 50 NAT | TECNOPOL | PP Homopolymer | OMIKRON |
| PANDEX TP-1318 | DIC Corporation | PUR, Unspecified | PANDEX |
| Sylvin 7833-85 Yellow 4206 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |