Corton® PDR 1623 HS
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Corton® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9yEbzq_Corton-PDR-1623-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Corton PDR 1623 HS is a 20% mica filled homopolymer polypropylene compound. It is a high flow injection moulding grade developed for rigid components requiring maximum rigidity good weld line strength and dimensional stability. It is stabilized to meet automotive heat ageing requirements (21 days at 150°C). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 16 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.90 to 1.3 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 113 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 80 | ||
| Shore D, 15 sec, 3.00 mm | 74 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 42.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 5.0 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 3600 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 19 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | 190 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.00 mm | 146 | °C | |
| 1.8 MPa, Unannealed, 3.00 mm | 90.0 | °C | |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 5.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong Nylon A1L04 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon, Unspecified | Shandong Nylon |
| China PPS hGR50 | Sichuan Deyang Chemical Co., Ltd | PPS | China PPS |
| ISPLEN® PP 086 U6E | REPSOL | PP Homopolymer | ISPLEN® |
| Sylvin 4200-88 Yellow 4192 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 3280-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |