Radiflam® A RV250K AE 121 C NAT 3489
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radiflam® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P2C9gp_Radiflam-A-RV250K-AE-121-C-NAT-3489.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA66 flame retardant injection moulding grade. 25% glass fiber reinforced. Natural colour. Suitable for parts requiring fire retardancy, medium stiffness and good mechanical resistance. Rated V-0 according to UL-94. ISO 1043 : PA66-T GF25 FR(17+72) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.57 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C, 2.00 mm | 4.0 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9500 | -- | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 110 | -- | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.9 | -- | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 8800 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 170 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 42 | 45 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 225 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 240 | -- | °C | ISO 306/B50 |
| Melting Temperature | 260 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | 0.0 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | V-0 | -- | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.00 mm | 960 | -- | °C | |
| 2.00 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.00 mm | 850 | -- | °C | |
| 2.00 mm | 850 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Salflex 815C | Salflex Polymers Ltd. | PP Copolymer | Salflex |
| ICORENE® 1761 V2 Black 9004 | ICO Polymers EMEA, A Division of A. Schulman | mMDPE | ICORENE® |
| INCOLOR PP BK002 | Infinity LTL Engineered Compounds | PP Homopolymer | INCOLOR |
| LNP™ THERMOCOMP™ OC006 compound | SABIC Innovative Plastics | PPS, Linear | LNP™ THERMOCOMP™ |
| Sarlink® TPE FM-2166 | Teknor Apex Company | TPE | Sarlink® TPE |