MAJORIS EE115T - 8938
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Os7Apy_MAJORIS-EE115T---8938.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EE115T - 8938 is a mineral reinforced, elastomer modified polypropylene compound intended for injection moulding. EE115T - 8938 has a controlled thermal expansion, suitable for high flow path/wall thickness ratios and gives a very nice surface. Thus suitable for exterior parts with reduced wall thickness. The product is UV stabilised. The product is available in dark grey (EE115T - 8938) and natural (EE115T) but other colours can be provided on request. EE115T - 8938 gives excellent paint ability by use of adhesive primers alone, or by use of other pre-treatments. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.990 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.85 - 0.95 | % | |
| Post Shrinkage | 0.15 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shaw D | 70 | ISO 868 | |
| Shaw D, 3 seconds | 61 | ISO 868 | |
| Shaw D, 5 seconds | 58 | ISO 868 | |
| Ball Indentation Hardness (H 132/10) | 35.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1150 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 17.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 7.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 5.0 | kJ/m² | ISO 179/1eA |
| -20°C | 6.5 | kJ/m² | ISO 179/1eA |
| 0°C | 29 | kJ/m² | ISO 179/1eA |
| 23°C | 45 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact (-40°C) | 4.5 | kJ/m² | ISO 180/1A |
| Multi-Axial Instrumented Impact Energy (-20°C, Total Penetration Energy) | 30.0 36.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 87.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 49.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 126 | °C | ISO 306/A |
| CLTE - Flow (23 to 80°C) | < 8.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Slow-Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressureScrew RPM: Slow to Medium |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEQUEL® 1480 | LyondellBasell Industries | TPO (POE) | SEQUEL® |
| Sindustris PP HF5255A | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| TOTAL Polystyrene Impact 3630 | TOTAL Refining & Chemicals | PS (MIPS) | TOTAL Polystyrene |
| Expandable PS D933B | INEOS Styrenics International SA | PS (EPS) | Expandable PS |
| Karina CRYSTAL PVC COMP. E 75/325-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |