Silamid® G10
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Roonamid a.s. |
| Trademark: | Silamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | c0uHx6_Silamid-G10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6, filled with graphite, improved sliding properties, increased rigidity and shape stability, optimal fluidity of mould. Injection mouldings with requirements of reducing friction coefficient, the sliding additive is released from moulding at wearing and acts as a lubricant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.19 | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | ||||
| Across Flow | 1.3 | 1.3 | % | |
| Flow | 1.2 | 1.2 | % | |
| Water Absorption (23°C, 24 hr) | 0.70 | 0.70 | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 4100 | 2200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 70.0 | 40.0 | MPa | ISO 527-2 |
| Flexural Modulus | 3500 | 1300 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 | 60 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 175 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | -- | °C | ISO 75-2/A |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 240 to 250 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLON IR 2200 | POLYMA Kunststoff GmbH & Co. KG | PC | POLYLON |
| Monprene® SP-12249 NAT | Teknor Apex Company | TPE | Monprene® |
| ICORENE® N2801 | ICO Polymers EMEA, A Division of A. Schulman | HDPE | ICORENE® |
| LG ABS EF378L | LG Chem Ltd. | ABS | LG ABS |
| TECHNYL eXten® D 219WFC V30 BLACK | Solvay Engineering Plastics | Nylon 610 | TECHNYL eXten® |