PermaStat® 300
| Category: | PC , Polycarbonate |
| Manufacturer: | RTP Company |
| Trademark: | PermaStat® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OqQtBv_PermaStat-300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ESD Protection - Permanently Anti-static - UL94 HB |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 - 0.90 | % | ASTM D955 |
| Moisture Content | 0.020 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Static Decay 1 | sec | FTMS 101C 4046.1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1650 | MPa | ASTM D638 |
| Tensile Strength | 44.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 1790 | MPa | ASTM D790 |
| Flexural Strength | 62.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 640 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 110 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 104 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 - 1.0E+12 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+8 - 1.0E+11 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | -28.9 | °C | |
| Processing (Melt) Temp | 221 - 243 | °C | |
| Mold Temperature | 65.6 - 121 | °C | |
| Injection Pressure | 41.4 - 68.9 | MPa |
| Injection instructions |
|---|
| Do not exceed 520 °F (270 °C) melt temperature.Desiccant Type Dryer Required. |
| Note Message | |
|---|---|
| 1 . | MIL-PRF-81705D, 5kV to 50 V, 12% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RELENE® M26500 | Reliance Industries Limited | LLDPE | RELENE® |
| Spartech Polycom SP7022 | Spartech Polycom | PC | Spartech |
| CALP FR913-1 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Cri-Line LS-715 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| DOMAMID® 66ST2 | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |