LNP™ LUBRILOY™ D20001 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OoCkLG_LNPLUBRILOYD20001compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY* D20001 is a compound based on Polycarbonate resin containing Flame Retardant, Proprietary Lubricant. Added features of this material include: Flame Retardant. Also known as: LNP* LUBRILOY* Compound D-FR ECO Product reorder name: D20001 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.50 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.60 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.57 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.53 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.12 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2550 | MPa | ASTM D638 |
| -- | 2600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 67.3 | MPa | ASTM D638 |
| Yield | 62.3 | MPa | ISO 527-2 |
| Fracture | 60.2 | MPa | ASTM D638 |
| Fracture | 54.5 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 4.5 | % | ASTM D638 |
| Yield | 4.3 | % | ISO 527-2 |
| Fracture | 6.5 | % | ASTM D638 |
| Fracture | 6.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2830 | MPa | ASTM D790 |
| -- | 2800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 103 | MPa | ASTM D790 |
| -- | 102 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.091 | ASTM D3702 Modified | |
| With Self-Static | 0.23 | ASTM D3702 Modified | |
| Wear Factor - Washer | 30.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 140 | J/m | ASTM D256 |
| 23°C 2 | 6.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1600 | J/m | ASTM D4812 |
| 23°C 3 | 100 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 51.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 97.2 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 89.4 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 94.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.6E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 6.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 249 - 260 | °C | |
| Middle Temperature | 254 - 266 | °C | |
| Front Temperature | 260 - 271 | °C | |
| Processing (Melt) Temp | 254 - 288 | °C | |
| Mold Temperature | 37.8 - 65.6 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEOFLON™ NP-20 | DAIKIN AMERICA, INC. | FEP | NEOFLON™ |
| Elexar® EL-8614 | Teknor Apex Company | TPE | Elexar® |
| ESENTTIA 05H82-AV | Polipropileno del Caribe S.A. | PP Homopolymer | ESENTTIA |
| KOPLA PA6 KRE1010 | KOPLA Co., Ltd. | Nylon 6+ABS | KOPLA PA6 |
| Pinnacle PP 2108 | Pinnacle Polymers | PP Impact Copolymer | Pinnacle PP |