POLYshine PBT D204 GF30 FR
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYshine |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OiA0mY_POLYshine-PBT-D204-GF30-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass fibre-reinforced Flame retarded |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.70 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.2 | % | |
| Flow | 0.30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 145 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.8 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 9000 | MPa | ISO 178 |
| Flexural Stress | 185 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 3.0 | kJ/m² | |
| 23°C | 3.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 210 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.00 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 960 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Softflex® 0809 | Network Polymers, Inc. | TPE | Softflex® |
| Sylvin 9734-73 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Tarflen® SM-B40 | Grupa Azoty S.A. | PTFE | Tarflen® |
| Vinylbond 95-950-75 | Colorite Polymers | PVC, Flexible | Vinylbond |
| DIALAC® TW21H | UMG ABS, Ltd. | SAS | DIALAC® |