NORYL™ PX0844 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OgxU2Y_NORYL-PX0844-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPE+PS blend. Unfilled. UL94 HB rated. Low water absorption. Hydrolytic stability. Dimensional stability. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 14 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2290 | MPa | ASTM D638 |
| -- | 2350 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 49.6 | MPa | ASTM D638 |
| Yield | 47.0 | MPa | ISO 527-2 |
| Break 3 | 44.0 | MPa | ASTM D638 |
| Break | 43.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield 4 | 3.0 | % | ASTM D638 |
| Yield | 2.9 | % | ISO 527-2 |
| Break 5 | 27 | % | ASTM D638 |
| Break | 43 | % | ISO 527-2 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2550 | MPa | ASTM D790 |
| 100 mm Span 7 | 2240 | MPa | ASTM D790 |
| -- | 2400 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 78.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 80.0 | MPa | ASTM D790 |
| Yield, 100 mm Span 9 | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/2C | ||
| -30°C | 10 | kJ/m² | |
| 23°C | 17 | kJ/m² | |
| Notched Izod Impact | |||
| -40°C | 130 | J/m | ASTM D256 |
| -30°C | 180 | J/m | ASTM D256 |
| 23°C | 230 | J/m | ASTM D256 |
| -30°C 10 | 10 | kJ/m² | ISO 180/1A |
| 23°C 11 | 18 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 40.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 120 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 6.40 mm | 121 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 100 mm Span 12 | 122 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 3.20 mm | 105 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 113 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 13 | 107 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 125 | °C | ISO 306/B50 |
| -- | 128 | °C | ISO 306/B120 |
| CLTE - Flow (0 to 100°C) | 7.4E-5 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 243 to 293 | °C | |
| Middle Temperature | 254 to 299 | °C | |
| Front Temperature | 266 to 304 | °C | |
| Nozzle Temperature | 277 to 304 | °C | |
| Processing (Melt) Temp | 277 to 304 | °C | |
| Mold Temperature | 71.1 to 98.9 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.6 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 2.6 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 120*10*4 mm |
| 13 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu RTV KE-3470 | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| Versalloy™ HC 9220-90 | PolyOne Corporation | TPE | Versalloy™ |
| Axiall PVC 830B | Axiall Corporation | PVC, Flexible | Axiall PVC |
| ESPRENE EPDM 301 | Sumitomo Chemical Co., Ltd. | EPDM | ESPRENE EPDM |
| Karina BLACK PVC COMP. 809D48/ 1-C-AC-AS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |