SABIC® HDPE B6246LS
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OYrgwe_SABIC-HDPE-B6246LS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE B6246LS is typically used in food and beverage packaging, offering good purity and organoleptics as well as recycle ability. It combines a high rigidity with very good processing performance, which offers potential for system cost reduction. The grade is typically used for the blow moulding of mono as well as multi layer bottles in several food markets, like fresh, pasteurised and ultra heat treated milk, sauces, orange juice, functional drinks, probiotics and other "daily shot" drinks. The material properties offer the possibility to reduce weight at good top load strength. This slip agent free grade is also typically used for the injection moulding of caps & closures for carbonated soft drinks and sparkling water as well as high environmental stress crack resistant applications, like UN-pails and UN-caps & closures. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.962 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.50 | g/10 min | |
| 190°C/21.6 kg | 46 | g/10 min | |
| 190°C/5.0 kg | 2.5 | g/10 min | |
| Environmental Stress-Cracking Resistance (10% Igepal CO-630, Compression Molded, F50) | 15.0 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 64 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1300 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00 mm, Compression Molded | 29.0 | MPa | |
| Break, 2.00 mm, Compression Molded | 18.0 | MPa | |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | > 1000 | % | ISO 527-2/1BA/50 |
| Flexural Modulus (2.00 mm, Compression Molded) | 1600 | MPa | ISO 178 |
| Flexural Stress (2.00 mm, Compression Molded) | 31.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C, Compression Molded | 7.0 | kJ/m² | |
| 23°C, Compression Molded | 13 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 89.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 129 | °C | ISO 306/A |
| Melting Temperature (DSC) | 135 | °C | ISO 11357-3 |
| Enthalpy Change | 225 | J/g | ISO 11357-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMSTER PE300J6 | Polyram Ram-On Industries | PET | RAMSTER |
| Moplen Z30S | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| THERMOLAST® M TM3ADT (Series: MC/AD1) | KRAIBURG TPE | TPE | THERMOLAST® M |
| CYCOLAC™ EX58 resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |
| SABIC® PPcompound 19T1040 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |