INEOS Wire & Cable BPD8167
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | INEOS Wire & Cable |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NwWAKw_INEOS-Wire-Cable-BPD8167.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BPD 8167 is a black filled polyethylene compound specially designed for overhead cable insulation. The compound is crosslinked by means of a "one-step" silane process. BPD 8167 is intended for the insulation of low voltage power cables. Thermal stability is ensured by addition of a carefully controlled quantity of antioxidant. It contains a dispersed carbon black to provide the necessary protection against outdoor weatherability according to the French specification NF C 33 209 Section 6.2 (07/96). The polymer system has been selected to give improved mechanical properties to meet French requirements for neutral phase Câble de Façade, particularly for anchorage and adherence testing (NFC 33209 - 07/96 - sections 6.5 and 6.8). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.948 | g/cm³ | ISO 1183/D |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.25 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 18.0 | MPa | IEC 811-1-1 |
| Tensile Strain (Break) | 300 | % | IEC 811-1-1 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Retention of Mechanical Properties - after weathering aging 1 | > 75 | % | NF C 33-209 |
| Tensile strength retention- 10 days (150°C) | > 75 | % | IEC 811-1-2 |
| Retention of Tensile Elongation - 10 days (150°C) | > 75 | % | IEC 811-1-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset | % | IEC 811-2-1 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Elongation 2(200°C) | % | IEC 811-2-1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | > 1.0E+3 | ohms·cm | ASTM D257 |
| Dielectric Constant (50 Hz) | 3.00 | ASTM D150 | |
| Dissipation Factor (50 Hz) | 1.5E-3 | ASTM D150 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| All the tests have been performed on cables extruded on a Nokia Maillefer BMA 45 30L/D monosil line with 1.5 % of a commercial mixture of vinyl trimethoxysilane, peroxide, crosslinking catalyst (ex : SILCAT R). The cables have been crosslinked 4 hours in water at 80 °C. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.015 | % | |
| Cylinder Zone 1 Temp. | 140 | °C | |
| Cylinder Zone 2 Temp. | 150 | °C | |
| Cylinder Zone 3 Temp. | 160 | °C | |
| Cylinder Zone 4 Temp. | 170 | °C | |
| Cylinder Zone 5 Temp. | 190 | °C | |
| Melt Temperature | 220 - 230 | °C | |
| Die Temperature | 220 | °C |
| Extrusion instructions |
|---|
| Zone 6 Temperature: 200°CZone 7 Temperature: 210°CHead Temperatures: 210-220-220°CScrew Cooling: 80°C |
| Note Message | |
|---|---|
| 1 . | Retention of tensile strength and elongation. |
| 2 . | 15 min, 30 N/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1001 TFE 15 | RTP Company | PBT | RTP |
| TOTAL Polypropylene PPH 10012 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| HiFill® PBT 2225 | Techmer Engineered Solutions | PBT | HiFill® |
| Petrotene® PP A3 T40 PRTA011 PH376 MSP | Petropol Industry and Trade of Polymers LTDA | PP Homopolymer | Petrotene® PP |
| POLYAXIS® LP 701 | A. Schulman Inc. | HDPE | POLYAXIS® |