Lucon® PA6110EM
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lucon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Nt65NK_LuconPA6110EM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Electromagnetic Interference (EMI) Shielding, EMI absorption Application Radar housing, Blind Spot Detection (BSD) shielding for automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 - 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 - 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 12.3 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | < 3.0 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 471 | MPa | ASTM D790 |
| Flexural Strength 4(6.40 mm) | 18.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 440 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 203 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+7 - 1.0E+11 | ohms | IEC 60093 |
| EMI Shielding Effectiveness (3.00 mm) | 3.00 - 6.00 | dB | ASTM D4935 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 100 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Rear Temperature | 230 - 250 | °C | |
| Middle Temperature | 240 - 270 | °C | |
| Front Temperature | 240 - 270 | °C | |
| Nozzle Temperature | 250 - 280 | °C | |
| Processing (Melt) Temp | 250 - 280 | °C | |
| Mold Temperature | 80 - 100 | °C | |
| Back Pressure | 0.00 - 0.981 | MPa | |
| Screw Speed | 40 - 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE FI1157 | Saudi Basic Industries Corporation (SABIC) | HDPE, HMW | SABIC® HDPE |
| Estane® 58810 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| Escorene™ Ultra UL 02133EN2 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Karina CLEAR PVC COMPOUND 80/229-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1t-7370 | Lehmann & Voss & Co. | Nylon 6/6T | LUVOCOM® |