INNOPOL® PP CS 1-1120 EP
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Inno-Comp Ltd. |
| Trademark: | INNOPOL® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NITTGz_INNOPOL-PP-CS-1-1120-EP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INNOPOL® CS 1-1120 EP is a 20 % talc-filled polypropylene homopolymer compound /PP-H TD20 (ISO 1043)/. This grade is available in nature and custom coloured form. Recommended application INNOPOL® CS 1-1120 EP is developed for producing injection moulded components for automotive industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 33.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 4.2 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break | 7.0 | % | ISO 527-2 |
| Flexural Modulus 1 | 2900 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 118 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 152 | °C | ISO 306/A120 |
| -- | 95.0 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Rear Temperature | 190 - 250 | °C | |
| Middle Temperature | 190 - 250 | °C | |
| Front Temperature | 190 - 250 | °C | |
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 10.0 - 50.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Hold pressure: 30 to 100 % of actual injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SNOLEN® IM 31/52 | JSC Gazprom neftekhim Salavat | HDPE | SNOLEN® |
| Stylac™ 220 | Asahi Kasei Chemicals Corporation | ABS | Stylac™ |
| ACCUTECH™ HP0339G15M15CL | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| KetaSpire® KT-851 | Solvay Specialty Polymers | PEEK | KetaSpire® |
| MAJORIS BT231 - 8229 | AD majoris | PP, Unspecified | MAJORIS |