AMPLIFY™ TY 1053H
| Category: | MAH-g , Functional Polymer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AMPLIFY™ TY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Da6hDx_AMPLIFY-TY-1053H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AMPLIFY™ TY 1053H Functional Polymer is a maleic anhydride grafted (MAH) polymer concentrate designed as a blend component for unmodified polyethylene. In tie layers for flexible packaging, AMPLIFY TY 1053H Functional Polymer promotes adhesion of polyethylene to barrier polymers such as polyamide and ethylene vinyl alcohol (EVOH). The functionality of this polymer also promotes adhesion between metal, polyolefins, cellulose, polyester, polycarbonate, glass, and foil. Typical blending levels in polyethylene let-down resin are 12-20% for EVOH and 6-12% for nylon. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.958 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238, ISO 1133 |
| MAH Graft Level 1 | Very High | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shaw A | 98 | ASTM D2240, ISO 868 | |
| Shaw D | 67 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Fracture 2 | 15.9 | MPa | ASTM D638 |
| Fracture | 15.9 | MPa | ISO 527-2/51 |
| Tensile Elongation | |||
| Fracture 3 | 300 | % | ASTM D638 |
| Fracture | 300 | % | ISO 527-2/51 |
| Flexural Modulus - 2% Secant | 924 | MPa | ASTM D790A, ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 129 | °C | ASTM D1525, ISO 306 |
| Melting Temperature (DSC) | 130 | °C | Internal method |
| Additional Information |
|---|
| Molded in accordance with ASTM D4976. |
| Note Message | |
|---|---|
| 1 . | Low: <0.25 wt%, Medium 0.25-0.5, High >0.5 wt%, Very High >1.0 wt%. |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA1212 PA1212 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 1212 | Shandong PA1212 |
| Sinvicomp SIG4561 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| VINIKA® CB88EA | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| NEFTEKHIM PP 1362S (HOXP2004) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Hylon® N1030HL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |