Trademark PE LLH1918
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Trademark Plastics Corporation |
| Trademark: | Trademark PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | N9ZKTO_Trademark-PE-LLH1918.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Applications:
Properties:
Additives:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 203 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 221 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 55.8 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 42.1 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 580 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 690 | % | ASTM D882 |
| Dart Drop Impact (25 µm, Blown Film) | 210 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 350 | g | ASTM D1922 |
| TD : 25 µm, blown film | 630 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.4 µm, Blown Film) | 35 | ASTM D2457 | |
| Haze (25.4 µm, Blown Film) | 19 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 191 - 218 | °C |
| Extrusion instructions |
|---|
| Blow-up ratio: 2:1 or higher |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6.6 7100 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Acculam™ Melaglas G5/G9 | Accurate Plastics, Inc. | Mel Phenolic | Acculam™ |
| Bergadur™ PBT-GL45 BK028 | PolyOne Corporation | PBT | Bergadur™ |
| Axiall PVC 9175 White 10 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Karina IVORY PVC COMPOUND 90900-35/1-Y-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |