Hiprolon® 70 MNWHL G50
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | Arkema |
| Trademark: | Hiprolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Mr1WvX_Hiprolon-70-MNWHL-G50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hiprolon ® 70 MNWHL G50 is a polyamide 6.10 produced from a renewable source and reinforced with 50% glass fiber. This black grade is designed for injection molding. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.46 | g/cm³ | ISO 1183 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.80 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14900 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 130 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 3.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 90 | kJ/m² | |
| 23°C | 95 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 221 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | °C | ISO 75-2/A |
| Melting Temperature | 222 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ISO Shortname | PA 610, MHLR, 27-140, GF 50 | ISO 1874 | |
| Renewable Carbon Conent | > 60 | % | ASTM D6866 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 260 to 300 | °C | |
| Mold Temperature | 60.0 to 110 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1200 T-70A | RTP Company | TPU-Polyether | RTP |
| Stanyl® TC153 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| TROGAMID® T BX7304 | Evonik Industries AG | Nylon 6/3T | TROGAMID® T |
| Ultramid® 8234G HS BK-102 | BASF Corporation | Nylon 6 | Ultramid® |
| APEX® 02-A0310A-107 | Teknor Apex Company | PVC, Semi-Rigid | APEX® |