Nypol® PA B3 G60 PRTA011 NT330
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Mm8Dmb_Nypol-PA-B3-G60-PRTA011-NT330.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6 in black color reinforced with 60% of fiberglass, high stiffness, high dimensional stability and excellent surface appearance of the molded part. With all these features, the product provides easy processing and easy filling cavities |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.63 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | 0.10 | -- | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.52 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 20000 | 15300 | MPa | ISO 527-2/1A |
| Tensile Stress (Yield) | 240 | 160 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 2.4 | 3.6 | % | ISO 527-2/1A |
| Flexural Modulus | 18800 | 13000 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact Strength | 14 | 20 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 215 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 220 | -- | °C | ISO 11357-3 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 220 | °C | |
| Middle Temperature | 230 | °C | |
| Front Temperature | 240 | °C | |
| Nozzle Temperature | 235 | °C | |
| Mold Temperature | 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Syncure™ S1060A Natural | PolyOne Corporation | XLPE | Syncure™ |
| FHR Polypropylene P5C4Z-090 | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |
| LNP™ STAT-LOY™ N30009 compound | SABIC Innovative Plastics | PC+ABS | LNP™ STAT-LOY™ |
| OLEFISTA™ QX0238D | Mitsubishi Chemical Performance Polymers, Inc. | Elastomer, Specialty | OLEFISTA™ |
| OTECH TPR OTR5505-Boot | OTECH Corporation | TPE | OTECH TPR |