LNP THERMOCOMP LF003 is a compound based on Polyetheretherketone resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound LF-1003 Product reorder name: LF003 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.80 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.0 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.0 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.79 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6930 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 137 | MPa | ASTM D638 |
| Yield | 125 | MPa | ISO 527-2 |
| Fracture | 137 | MPa | ASTM D638 |
| Fracture | 125 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.9 | % | ASTM D638 |
| Yield | 2.4 | % | ISO 527-2 |
| Fracture | 3.1 | % | ASTM D638 |
| Fracture | 2.4 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 62700 | MPa | ASTM D790 |
| -- | 7000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 200 | MPa | ASTM D790 |
| -- | 209 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 1 | 6.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 850 | J/m | ASTM D4812 |
| 23°C 2 | 54 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 14.6 | J | ASTM D3763 |
| -- | 3.10 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 329 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 3 | 325 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 259 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 244 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 4.9E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 4.8E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 3.1E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sasol Polymers PE HR411/06 | Sasol Polymers | LLDPE | Sasol Polymers PE |
| Cevian®-V SKG20 | Daicel Polymer Ltd. | ABS | Cevian®-V |
| Clariant Nylon 6/6 6622-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Formolene® 5102KR | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| SQUARE® SCR2530-30A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |